CHEM-CRETE® MCE

Chem-Crete® MCETM (MCETM) is a multi-crystalline admixture and an innovative concrete waterproofing material. It is a significant step forward in increasing long-term concrete performance and durability that functions effectively with both Portland Cement and 1L (Limestone) Cement. It is categorized according to ASTM C494/C494M as Type S admixture. MCETM is a multi-compound aqueous solution that is mixed into fresh concrete during the batching process resulting in a uniform distribution throughout the cement paste. MCETM cures within cement hydration stages forming a network of hygroscopic and hydrophilic crystals (pore blocking) coupled with molecular layers (pore lining) that become an integral part of concrete structure. The porosity and permeability of resulting concrete structure is significantly decreased leading to concrete protection against nearly all types of water-related attacks and thereby enhances both the concrete durability and structure sustainability. The material performance has been shown through extensive laboratory studies and field trials.

A key feature of MCETM is its ability to actively manage water in the concrete thereby minimizing or eliminating moisture-related damage including freeze/thaw cycling and alkali silica reactivity (ASR). In addition, by controlling the amount of water entering the concrete, chloride intrusion is minimized, mold growth is inhibited, and overall concrete sustainability is greatly enhanced. Furthermore, MCETM improves the workability, enhances the hydration of the cement, and increases the strength of fully cured concrete. MCETM may allow for the elimination of fly ash in concrete for ASR mitigation.

MCETM is applicable to both central mixed and ready mixed plant operations.  The method of incorporating the material into the concrete during the batching process is somewhat dependent on the specific batching equipment. However, MCETM is generally added into the water feed similar to chemical admixtures.

MCETM can be added to a concrete mix at a batching plant, in a volumetric mixing truck or at a job site similar to adding typical chemical admixtures.

Request a Quote
Category:

DOWNLOADS

Description

Multi-crystalline Admixture for Improving Concrete Durability and Performance, built into the concrete mix

What It Is

Chem-Crete® MCETM (MCETM) is a multi-crystalline admixture and an innovative concrete waterproofing material. It is a significant step forward in increasing long-term concrete performance and durability that functions effectively with both Portland Cement and 1L (Limestone) Cement.

TYPICAL APPLICATIONS

Integral durability enhancement for fresh concrete; the material is added during batching and becomes part of the concrete matrix.

Key Facts

  • FORM
    Liquid admixture
  • DOSAGE
    1–2% of cement weight*
  • CONCRETE
    Fresh / new
  • ROLE
    Durability + performance

Advantages, Features & Benefits

  • Type S admixture (ASTM C494/C494M) that functions effectively with both Portland Cement and 1L (Limestone) Cement
  • An innovative sustainable solution to moisture-related distresses that is compatible with most water-reducers and air-entrainment materials used in concrete mix design.
  • A long-term protection internal waterproofing and moisture blocking for concrete against water penetration, in all its phases (vapor, liquid and ice).
  • A dynamic crystallization system that interacts with water in its three phases which enhances water management (reduced liquid and water vapor movement within the hardened concrete and reduced ice adhesion).
  • Reduction in PCC capillary porosity and water permeability (by 2-3 orders of magnitudes).
  • Reduced jet fuel and oil penetration through concrete surfaces.
  • Hydrophobicity characteristics that help preventing water from wetting and saturating concrete surfaces.
  • Reduced ice adhesion and hence reduced consumption of deicing salts & agents.
  • Preventing freezing of freshly cast concrete: MCETM has a distinguished and unique thermal behavior of preventing water freezing in MCE-dosed fresh concrete under severe continuous freezing conditions. Figure 1 shows that the temperature of MCE modified fresh concrete remained above freezing temperature for about 2 months (when the concrete is continuously subjected to -50oF), while the temperature of the control sample dropped to a value below freezing within three days.
  • Improved freeze-thaw durability. Experimental data of IDOT C4 mix concrete samples with 2% MCETM indicate a reduction of mass loss by 91.6% and an increase in the relative dynamic modulus by 20.3%. The results of % mass loss presented in figure 2 are from an independent laboratory testing according to ASTM C666.
  • Reduced chloride ion penetration from deicing salts, increased concrete electrical resistivity by a percentage over 90% and reduced associated steel corrosion and paste degradation.
  • Reduced Alkali Silica Reactivity (ASR) problems and silicate dusting: The percentage reduction in length change due to ASR in 2% MCE- dosed concrete including reactive aggregates can be in the range of 45-77% (according to ASTM C1567, 28 days testing). Fig. 3 shows that MCETM meets the requirement of ASTM C1293 (long term testing) on length change by not going above the 0.04% ASTM limit (for one year), see Fig. 3
  • Reduced fungal and microbial growth according to anti-fungal and microbial test method MIL-SDD810G (reduced mold associated problems).
  • Enhanced workability and finishability: the effective compounds of MCETM enhance concrete slump as indicated in fig.4. The results in Fig. 4 are for concrete mix designs with and without fly ash, obtained by an independent laboratory testing
  • Reduced shrinkage and surface cracking.
  • Helps concrete stay whiter & brighter (Albedo Surface).

Uses

  • Highways, Streets, Roads and Manholes.
  • Bridges, Tunnels and Retaining Walls.
  • Slabs-on-Grade and Below Grade Structures.
  • Precast/tilt-up and Cast-in-Place Concrete.
  • Concrete Parking Lots, Sidewalks and Driveways.
  • Dams, Reservoirs, Canals and Waterways.
  • Water Tanks and Treatment Plants.
  • Secondary Containment Structures.
  • Sea Walls and Port Facilities.
  • Commercial and Residential Structures.
  • Parking Structures (Above and Below Grade).
  • Basements, Foundations, Floors, Patios and Pools.

Packaging

Product Packaging
CHEM-CRETE MCETM 5 GAL (18.925 LITER) PAIL
55 GAL (208 LITER) DRUM
265 GAL (1000 LITER) TOTE

Technical

Physical Properties
Specific Gravity 1.1 – 1.2
Viscosity 2.4 centipoises
Freezing Point 24ºF (-4.4°C)
Boiling Point 219ºF (104 °C)
Color Clear
Environmental Hazards None
Odor None
Toxicity None
Fumes None
Flammability None
  Product Performance is tested according to the following test standards:
  • Type S admixture (ASTM C494/C494M) that functions effectively with both Portland Cement and 1L (Limestone) Cement
  • CRD-48-92 US Army Corps of Engineers Standard Test Method for Water Permeability of Concrete
  • ASTM D6489-99 Determining the Water Absorption of Hardened Concrete Treated with a Water Repelling Coating.
  • ASTM C642-97 Standard Test Method for Density, Absorption, and Voids in Hardened Concrete.
  • ASTM C642-97 Density, Absorption, and Voids in Hardened Concrete.
  • ASTM C1202-91 Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration.
  • AASHTO T260 Sampling and Testing for Chloride Ion in Concrete and Concrete Raw Materials.
  • AASHTO T277 Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration.
  • AASHTO T259-00 Resistance of Concrete to Chloride Ion Penetration.
  • ASTM C1218 Water-Soluble Chloride in Mortar and Concrete.
  • ASTM C672-98 Scaling Resistance of Concrete Surfaces Exposed to Deicing Chemicals.
  • ASTM C457-98 Microscopical Determination of Parameters of the Air-Void System in Hardened Concrete.
  • MIL-STD-810G Fungal Resistance According to Test Method Standard for Environmental Engineering Considerations and Laboratory Tests.
  • ASTM D7234 Pull-Off Adhesion Strength of Coatings on Concrete.
  • ASTM D4541-95 Pull-Off Strength of Coatings Using Portable Adhesion Testers.
  • ASTM C1583 Bond Strength or Tensile Strength of Overlay Materials by Direct Tension.
  • ASTM F609-96 Standard Test Method for Using a Horizontal Pull Slipmeter (HPS).
  • ASTM E303-93 Measuring Surface Frictional Properties Using the British Pendulum Tester.
  • ASTM D7234 Standard Test Method for Pull-Off Adhesion Strength of Coatings on Concrete Using Portable Pull-Off Adhesion Testers.
  • ASTM C666-97 Resistance of Concrete to Rapid Freezing & Thawing.
  • ASTM C1567 Standard Test Method for Determining the Potential Alkali-Silica Reactivity of Combinations of Cementitious Materials and Aggregate (Accelerated Mortar-Bar Method).
  • ASTM C1293 Standard Test Method for Determination of Length Change of Concrete Due to Alkali-Silica Reaction.

Application

Method of Application: MCETM is shipped in a ready-to-use state, with no additional preparation prior to use.  The product is simply mixed with the concrete at the time of batching and is applicable to both ready-mixed and central mix production. 

Blending: The MCETM can be introduced into the water stream at the time of batching or added to fresh concrete mixture at the job site.

Consumption: 1% of the cement weight or 13.8 oz/cwt (453 grams MCE/100 lbs cement).

Cleaning: clean all equipment and tools with fresh clean water immediately after use.

Storage

Two years shelf life when stored in a cool, dry place in its original unopened container. Always agitate or stir the product’s container before using it. DO NOT ALLOW THE PRODUCT TO FREEZE. Repeated freezing & thawing might cause damage to the product.  

Safety

As with all construction chemical products, adequate precautions and care must be taken during usage and storage.  Avoid direct contact with foodstuff, eyes, skin, and mouth.  Any direct contact with skin, eyes, etc. should be washed thoroughly with clean running water and soap.

Always wear protective goggles and gloves. In case of eye contact, flush for 15 minutes with warm water. KEEP OUT OF REACH OF CHILDREN.

Warranty

LIMITED WARRANTY:   International Chem-Crete Inc. warrants that, at the time and place we make shipment, our materials will be of good quality and will conform to our published specifications in force on the date of acceptance of the order.

DISCLAIMER:   The information contained herein is included for illustrative purposes only and, to the best of our knowledge, is accurate and reliable. International Chem-Crete Inc. is not under any circumstances liable to connection with the use of information. As International Chem-Crete Inc. has no control over the use to which others may put its products, it is recommended that the products be tested to determine the suitability for specific applications and/or our information is valid in particular circumstances. Responsibility remains with the architect or engineer, contractor and owner of the design, application, and proper installation of each product. Specifier and user shall determine the suitability of the product for a specific application and assume all responsibility in connection therewith.

NO OTHER WARRANTIES EXPRESS OR IMPLIED SHALL APPLY INCLUDING ANY WARRANTY OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE. CHEM-CRETE SHALL NOT BE LIABLE UNDER ANY LEGAL THEORY FOR SPECIAL OR CONSEQUENTIAL DAMAGES. CHEM-CRETE SHALL NOT BE RESPONSIBLE FOR THE USE OF THIS PRODUCT IN A MANNER TO INFRINGE ON ANY PATENT OR ANY OTHER INTELLECTUAL PROPERTY RIGHTS HELD BY OTHERS. MJ17922-1

Gallery

Content coming soon.

Reviews

There are no reviews yet.

Only logged in customers who have purchased this product may leave a review.

Related products

MENU